    55mm Porcelain Evaporating Dish, Flat Bottom


    Porcelain flat-bottomed evaporating dish with a diameter of 55 mm.
    Manufactured in the Czech Republic by JIPO.
    Material properties:
    - High mechanical strength
    - Low longitudinal thermal expansion
    - Maximum working temperature: with unglazed articles up to 1350 °C and with glazed articles up to 1100 °C.

    Please see technical data sheet for dimensions and more information.

    €9.29 Tax incl.
    €7.68 Tax excl.
    Spain 21% VAT; The final tax applicable may vary according to the country of destination.

    18 ml Porcelain Evaporating Dish, Flat Bottom

    The laboratory porcelain is highly resistant to fire and direct flame. The evaporating dish is used for the separation of solutions by evaporation through the application of heat and, at higher temperatures, it is a support for carbonizing or melting chemical substances and compounds.

    The recipient has a pouring spout and is fully enamelled except for the lower outer base.

    Utensil for jewellery and silverware professionals, metallurgical and ceramics companies, pharmacies, catering, kitchens and laboratories in general.

    Technical characteristics of JIPO porcelain

    JIPO is a distinguished Czech brand recognized for the high quality of its products in accordance with EN 1183 and ISO 1775 standards.

    The manufactured porcelain material is within the group C110 according to the Czech State Standard (CSN 60672-3 standard) and meets the parameters of the highest working requirements due to its high quality, good chemistry and heat resistance. Its composition is clay, quartz and feldspar (3AL2O3. 2SiO2).

    Technical properties
    High softening temperature, which makes it possible to work with:
    unglazed products can be used at temperatures up to 1350 °C / 2462 °F
    glazed products at temperatures of up to 1000 °C / 1832 °F

    Other technical properties:
    Density = 2.4 g/cm³
    Resistance of unglazed products (70 MPa) bending strength
    Thermal conductivity (Wm-1 . K-1) = 1.3
    Resistance to alkalis, 99.96%.
    Resistance to acids, 99.99%.
    Hardness according to Mohs 7-8
    Resistance to traction, 400 Kp/cm²
    Resistance to compression 3500 Kp/cm²
    Resistance to bending minimum 500 Kp/cm²
    Water absorption capacity 0%

    Data sheet

    Product Type
    Evaporation Dish
    18 ml
    Rim Shape
    Flat Finish with Spout
    Body Shape
    Cylindrical-Conical Shaped
    Height Shape
    Low Form - Shallow Form
    Bottom Shape
    Flat bottom
    22 mm
    55 mm Ø
    Enamelled / vitrified / glazed
    Glazed inside and outside, except the base of the mortar
    by Unit