1,000ml Glass Beaker, Low Form
Price €11.30 €9.34 Tax excl.
Graduated beaker with spout and a capacity of 100 ml, low shape.
SIMAX brand: made in the Czech Republic (EU) of borosilicate glass according to ISO and DIN standards.
Laboratory container with white graduation and writing area.
Graduation range is 25 ml and with measurement up to 75 ml.
Silk-screened measurements are approximate, as they are not calibrated.
Autoclave
The thickness of the glass allows for hot work
Available in low and high shapes in different sizes.
See description or technical data sheet for more information on characteristics.
Manufactured according to DIN 12331 and ISO 3819 in the Czech Republic, SIMAX brand, EU – CE.
It can be cleaned by autoclave.
Capacity | Height | Diameter | Graduation range | Graduated up to |
5 ml | 30 mm | 22 mm | Not graduated | |
10 ml | 35 mm | 26 mm | Not graduated | |
25 ml | 50 mm | 34 mm | 10 ml | 20 ml |
50 ml | 60 mm | 42 mm | 15 ml | 40 ml |
100 ml | 70 mm | 50 mm | 25 ml | 75 ml |
150 ml | 80 mm | 60 mm | 25 ml | 125 ml |
250 ml | 95 mm | 70 mm | 50 ml | 200 ml |
400 ml | 110 mm | 80 mm | 100 ml | 300 ml |
600 ml | 125 mm | 90 mm | 100 ml | 500 ml |
1,000 ml | 145 mm | 105 mm | 100 ml | 800 ml |
2,000 ml | 185 mm | 130 mm | 250 ml | 1,500 ml |
3,000 ml | 210 mm | 150 mm | 250 ml | 2,500 ml |
5,000 ml | 270 mm | 170 mm | 500 ml | 4,000 ml |
10,000 ml | 350 mm | 217 mm | 1000 ml | 8,000 ml |
This glass is distinguished by its very good chemical resistance to water, salt solutions, acids, bases and organic solvents. It is only attacked by hydrofluoric acid and, at high temperatures, by strong bases and phosphoric acid.
Chemical composition
80.00% Silica; SiO2
12.50% Boron trioxide; B2O3
2.40% of Aluminium oxide; Al2O3
3.80% of sodium oxide; Na2O
1.00% of potassium oxide; K2O
0.30% of iron oxide; Fe2O3
Chemical resistance
Hydrolytic according to DIN 12111 and ISO 719: Class 1
Acid-resistant according to DIN 12116: Class 1
Alkaline according to DIN 52322 and ISO 695: Class 2
Physical properties:
Coefficient of linear expansion: 3.3
Processing temperature: 534° C
Upper annealing temperature: 550° C
Lower annealing temperature: 494° C
Maximum working temperature: 500° C