Tall beaker with spout with a capacity of 400 ml.
Graduated laboratory beaker with white silk-screen printing.
Simax brand: made in the Czech Republic (EU) in borosilicate glass 3.3 with white graduation and writing area.
Capacity 400 ml
Height 130 mm
Diameter Ø 70 mm
Graduation intervals every 100 ml up to 300 ml.
400ml Tall Form Glass Beaker
Code
Tall beaker with spout with a capacity of 400 ml.
Graduated laboratory beaker with white silk-screen printing.
Simax brand: made in the Czech Republic (EU) in borosilicate glass 3.3 with white graduation and writing area.
Capacity 400 ml
Height 130 mm
Diameter Ø 70 mm
Graduation intervals every 100 ml up to 300 ml.
€6.28 tax incl.
€5.19 Tax excl.
Spain 21% VAT; The final tax applicable may vary according to the country of destination.
High-form graduated beaker of 400ml capacity.
Manufactured according to DIN 12331 and ISO 3819 in the Czech Republic - EU - CE.
It can be cleaned by autoclave.
| Capacity | Height | Diameter | Graduation range |
Graduated up to |
| 50 ml | 70 mm | 38 mm | 15 ml | 40 ml |
| 100 ml | 80 mm | 48 mm | 25 ml | 75 ml |
| 150 ml | 95 mm | 54 mm | 25 ml | 125 ml |
| 250 ml | 120 mm | 60 mm | 50 ml | 200 ml |
| 400 ml | 130 mm | 70 mm | 100 ml | 300 ml |
| 600 ml | 150 mm | 80 mm | 100 ml | 500 ml |
| 1,000 ml | 180 mm | 95 mm | 100 ml | 800 ml |
| 2,000 ml | 240 mm | 120 mm | 250 ml | 1,500 ml |
| 3,000 ml | 280 mm | 135 mm | 250 ml | 2,500 ml |
Dimensions covered by drawings
General properties of borosilicate glass 3.3
This glass is distinguished by its very good chemical resistance to water, salt solutions, acids, bases and organic solvents. It is only attacked by hydrofluoric acid and, at high temperatures, by strong bases and phosphoric acid.
Chemical composition
80.00% Silica; SiO2
12.50% Boron trioxide; B2O3
2.40% of Aluminium oxide; Al2O3
3.80% of sodium oxide; Na2O
1.00% of potassium oxide; K2O
0.30% of iron oxide; Fe2O3
Chemical resistance
Hydrolytic according to DIN 12111 and ISO 719: Class 1
Acid-resistant according to DIN 12116: Class 1
Alkaline according to DIN 52322 and ISO 695: Class 2
Physical properties:
Coefficient of linear expansion: 3.3
Processing temperature: 534° C
Upper annealing temperature: 550° C
Lower annealing temperature: 494° C
Maximum working temperature: 500° C
Data sheet
- Product Type
- Beaker
- Material
- Borosilicate Glass
- Capacity
- 400 ml
- Body
- 70 mm Ø
- Rim Shape
- Flat Finish with Spout
- Body Shape
- Cylindrical Shaped
- Height Shape
- Tall Form
- Bottom Shape
- Flat bottom
- Height
- 130 mm
- Graduation
- Colour Printed Scale
- Screen Print Colour
- White
- Scaling intervals
- Graduated to approximate volumes
- Standard
- DIN 12331 - ISO 3819
- Sale
- by Unit