150 ml Low Form Glass Beaker

150ml Low Form Glass Beaker

Code

Graduated beaker with spout and a capacity of 150 ml, low shape.
SIMAX brand: made in the Czech Republic (EU) of borosilicate glass according to ISO and DIN standards.
Laboratory container with white graduation and writing area.
Graduation range is 25 ml and with measurement up to 125 ml.
Silk-screened measurements are approximate, as they are not calibrated.
Autoclave
The thickness of the glass allows for hot work
Available in low and high shapes in different sizes.
See description or technical data sheet for more information on characteristics.

€4.50 tax incl.
€3.72 Tax excl.
Spain 21% VAT; The final tax applicable may vary according to the country of destination.
Add to compare

150ml Glass Break, low form

Manufactured according to DIN 12331 and ISO 3819 in the Czech Republic, SIMAX brand, EU – CE.
It can be cleaned by autoclave.

Capacity Height Diameter Graduation range Graduated up to
5 ml 30 mm 22 mm Not graduated
10 ml 35 mm 26 mm Not graduated
25 ml 50 mm 34 mm 10 ml 20 ml
50 ml 60 mm 42 mm 15 ml 40 ml
100 ml 70 mm 50 mm 25 ml 75 ml
150 ml 80 mm 60 mm 25 ml 125 ml
250 ml 95 mm 70 mm 50 ml 200 ml
400 ml 110 mm 80 mm 100 ml 300 ml
600 ml 125 mm 90 mm 100 ml 500 ml
1,000 ml 145 mm 105 mm 100 ml 800 ml
2,000 ml 185 mm 130 mm 250 ml 1,500 ml
3,000 ml 210 mm 150 mm 250 ml 2,500 ml
5,000 ml 270 mm 170 mm 500 ml 4,000 ml
10,000 ml 350 mm 217 mm 1000 ml 8,000 ml

General properties of borosilicate glass 3.3

This glass is distinguished by its very good chemical resistance to water, salt solutions, acids, bases and organic solvents. It is only attacked by hydrofluoric acid and, at high temperatures, by strong bases and phosphoric acid.

Chemical composition
80.00% Silica; SiO2
12.50% Boron trioxide; B2O3
2.40% of Aluminium oxide; Al2O3
3.80% of sodium oxide; Na2O
1.00% of potassium oxide; K2O
0.30% of iron oxide; Fe2O3

Chemical resistance
Hydrolytic according to DIN 12111 and ISO 719: Class 1
Acid-resistant according to DIN 12116: Class 1
Alkaline according to DIN 52322 and ISO 695: Class 2

Physical properties:
Coefficient of linear expansion: 3.3
Processing temperature: 534° C
Upper annealing temperature: 550° C
Lower annealing temperature: 494° C
Maximum working temperature: 500° C

Data sheet

Product Type
Beaker
Material
Borosilicate Glass
Capacity
150 ml
Body
60 mm Ø
Rim Shape
Flat Finish with Spout
Body Shape
Cylindrical Shaped
Height Shape
Low Form - Shallow Form
Bottom Shape
Flat bottom
Height
150 mm
Graduation
Colour Printed Scale
Screen Print Colour
White
Scaling intervals
Graduated to approximate volumes
Standard
DIN 12331 - ISO 3819
Sale
by Unit


Related Products



You might also like

Welcome to LABComercial! This website uses its own cookies, third-party cookies and other technologies, such as tags for functional purposes, statistical analysis, personalisation of your browsing habits and provide you customised content. To change your preferences or for further information on the use of these cookies, please see the following sections: See cookie policy
Accept all Reject all Configure cookies